1.1274 | C100S +QW +T Prior austenite grain boundaries
| Numeric designation | 1.1274 |
|---|---|
| Chemical designation | C100S |
| State | 1.1274 | C100S +QW +T Prior austenite grain boundaries |
| Etching | PAG HT |
This hypereutectoid steel (sheet material with cross-section = 2 x 30 mm) with 0.98 % carbon (measured with OES; target: 0.95 – 1.05 %) was austenitised at 810 °C for 30 min, quenched in water and then tempered at 250 °C for 2 hours.
The unalloyed and low tempered steel was successfully etched onto former austenite grain boundaries using ‘PAG HT’.
The copper precipitate is polished off on a stationary, wet OPS disc (ChemTec). Depending on the alloy, 25% ammonia and a cotton swab are required to remove the copper precipitate.
Parameters:
- Etchant PAG HT (made by Schmitz)
- 3+3 min (image)
- +3+1+5 min (image 2)
- Room temperature
Click here to go to the article in our online shop
Fe-Base
1.1221 | C60E +I Prior austenite grain boundaries
1.1269 | C85S +QW +T Prior austenite grain boundaries
1.7076 | 32CrB4 +Q Prior austenite grain boundaries
1.1221 | C60E +QW +T Prior austenite grain boundaries
1.1191 | C45E +QW +T Prior austenite grain boundaries
1.7220 | 34CrMo4 +Q Prior austenite grain boundaries
1.7220 | 34CrMo4 +QT (12.9) Prior austenite grain boundaries
1.7076 | 32CrB4 +QT (12.9) Prior austenite grain boundaries
1.5511 | 35B2 +QT (9.8) Prior austenite grain boundaries