1.4765 | X8CrAl25-5 AlN precipitations
| Numeric designation | 1.4765 | UNS S44600 | AISI 446 |
|---|---|
| Chemical designation | 1.4765 | X8CrAl25-5 AlN |
| State | AlN precipitations |
| Etching | unetched |
The micrographs show the “heat conductor alloy” after several months of use at approx. 1050 °C. Locally, there was drastic nitrogenisation with the formation of unusually coarse aluminium nitrides.
The SEM images show a cleavage fracture surface of the coarse-grained microstructure with the nitrides.