1.2379 | X153CrMoV12 built-up welding with crack
| Numeric designation | 1.2379 |
|---|---|
| Chemical designation | X153CrMoV12 |
| State | built-up welding with crack |
| Etching | 3 % Nital |
Here, shrinkage cavities (insufficient degree of forging) in the area near the surface are the cause of the crack in the weld. The welder is not to blame.