1.2379 | X153CrMoV12 Forging defect
| Numeric designation | 1.2379 |
|---|---|
| Chemical designation | X153CrMoV12 |
| State | Auftragsgeschweißt |
| Etching | 3% Nital |
Finding: The cause of cracking in the built-up welding is due to residual shrinkage cavities of the base material which have not been forged together.