Back (Additive Manufacturing (AM))
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 58 J/mm³ | BUR 21.6 cm³/h
| Numeric designation | Titan Grade 23 | 3.7165 |
|---|---|
| Chemical designation | Ti6Al4V ELI |
| State | Additive manufactured by means of L-PBF |
| Etching | Kroll |
The microstructure consists of martensite. There are layer bonding defects (~ 200 µm) extending over several layers as well as pores. At this high build-up rate, there are not yet completely melted powder particles. Etching was carried out with Kroll for approx. 2 min.
- Laser class 400 W
- Beam diameter 130 µm
- Layer thickness 30 µm
- VED 58 J/mm³
- Build-up rate 21.60 cm³/h
- Relative density > 99.8
- Powder grain fraction -45/+15 µm
Additive Manufacturing (AM)
WE43 | PF -53/+15 µm | VED 139 J/mm³ | BUR 6,5 cm³/h
WE43 | PF -53/+15 µm | VED 101 J/mm³ | BUR 7,1 cm³/h
WE43 | PF -53/+15 µm | VED 238 J/mm³ | BUR 3 cm³/h
WE43 | PF -53/+15 µm
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 117 J/mm³ | BUR 11 cm³/h
Titanium Grade 23 | Ti6Al4V ELI | PF -45/+15 µm | VED 50 J/mm³ | BUR 9 cm³/h
CC484K | CuSn12Ni2 L-PBF on 1.7225 | 42CrMo4
1.4404 | X5CrNoMo17-12-2 | PF -45/+15 µm | VED 41,67 J/mm³ | BUR 21,60 cm³/h